| ArticleName |
Structure and mechanical properties of a 132 mm thick welded joint of low-carbon Nb and
Nb + Ti heavy plate steel after TM+AcC |
| Abstract |
Offshore low-carbon microalloyed steel heavy plates of grades EH36/S460ML with a thickness of 132 mm was produced at the heavy plate hot rolling complex 4200 of NLMK DanSteel steel works. Steel heavy plates were microalloyed with Nb/Nb + Ti and were produced using thermomechanical controlled process with intermediate and final accelerated cooling. Produced heavy plates were bended into tube sections for the foundations of offshore wind generators. Cold bending was done with diameter 10 m and submerged arc welding (SAW) was performed with heating input 35 ± 5 kJ/cm. Samples of full thickness welded joints were used for investigations and qualification testing, incl. tensile tests, hardness, low temperature toughness and fatigue CTOD tests. Positive results of tests and investigations were used for classification of heavy plate grades ASTM A131 EH36/EN 10025-4:2019 S460ML, S420ML, S355ML in maximal thickness up to 132 mm and are recommended to be used in offshore contractions |
| References |
1. Ghosh S., Mula S. Thermomechanical processing of low carbon Nb–Ti stabilized microalloyed steel: Microstructure and mechanical properties. Materials Science and Engineering: A. 2015. Vol. 646. pp. 218–233.
2. Fukunaga K., Yoshii K.-I., Shinohara Y., Yoneda T. et al. High strength TMCP steel plate for offshore structure with Excellent HAZ toughness at welded joints. Nippon Steel & Sumitomo Metal Technical Report. 2015. Vol. 10. pp. 43–49.
3. Igwemezie V., Mehmanparast A., Kolios A. Current trend in offshore wind energy sector and material requirements for fatigue resistance improvement in large wind turbine support structures A review. Renewable and Sustainable Energy Reviews. 2019. Vol. 101 (C). pp. 181–196.
4. Abbas M., Shafiee M. An overview of maintenance management strategies for corroded steel structures in extreme marine environments. Marine Structures. 2020. Vol. 71. pp. 1–35.
5. Borthwick A., Wu X., Hu Y., Li Y. et al. Foundations of offshore wind turbines: A review. Renewable and Sustainable Energy Reviews. 2019. Vol. 104. pp. 379–393.
6. Goli-Oglu E. A. Weldability of structural steels S355MLO and S420MLO with a thickness of up to 82 mm, produced by the TMP + AC method and used for new generation offshore wind generators. Problemy chernoy metallurgii i materialovedeniya. 2021. No. 4. pp. 76–85.
7. EN 10225-1:2019. Weldable structural steels for fixed offshore structures. Technical delivery conditions. Part 1: Plates. Brussels, 2019. 64 p.
8. Goli-Oglu E. A., Filatov A. N. Microstructure and mechanical properties of 122 mm welded joints of low-carbon microalloyed heavy plate steel after TM + ACC. Chernye Metally. 2022. No. 10. pp. 52–60.
9. Offshore standards. DNV-OS-B101. Metallic materials. Oslo, 2023. 161 p.
10. Goli-Oglu E. A. Production of structural steel heavy plates up to 100 mm by TMCP with final accelerated cooling for wind generators and bridgebuildings. Part 1. Chernye Metally. 2021. No. 5. pp. 17–22.
11. Goli-Oglu E. A. Production of structural steel heavy plates up to 100 mm by TMCP with final accelerated cooling for wind generators and bridgebuildings. Part 2. Chernye Metally. 2021. No. 7. pp. 50–55.
12. Goli-Oglu E. A., Mezinov S. M., Filatov A. N. Heating of large-sized slabs up to 400 mm thick in the NLMK DanSteel`s latest generation heating furnace. Stal. 2023. No. 1. pp. 38–44.
13. Bokachev Yu., Sarkits I., Goli-Oglu E. NLMK-DanSteel: production of thick plates and heavy slabs. Metallurg. 2014. No. 5. pp. 67–70.
14. ASTM Book. Section 1: Iron and Steel Products. ASTM A131/A131M-19. Standard Specification for Structural Steel for Ships. Houston, 2023. 866 p.
15. Mulazzani D. Evolution of Offshore Foundations. Available at: https://www.offshorewind.biz/2021/02/02/evolution-of-offshore-foundations/ (accessed: 30.06.2022).
16. Goli-Oglu E. Heavy plates for offshore wind. Stahl und Eisen. 2022. No. 6. pp. 51–57.
17. Vadholm T. Investigation of low temperature toughness and crack initiation in welded structural steels. Norwegian University of Science and Technology. Trondheim, 2014. 239 p.
18. Østby E., Thaulow C., Akselsen O. M. Fracture toughness scatter and effect of constraint in weld thermal simulated HAZ microstructures at –60 °C. Offshore Proceedings of the 21st International Offshore and Polar Engineering Conference 2011. Maui, Hawaii: ISOPE. Vol. 4. pp. 443–448.
19. Li Y., Baker T. N. Effect of morphology of martensite-austenite phase on fracture of weld heat affected zone in vanadium and niobium microalloyed steels. Materials Science and Technology. 2010. Vol. 26, Iss. 9. pp. 1029–1040.
20. Conde F. F., Pinto H. C., Masoumi M., Avila J. A. Effect of textures and microstructures on the occurrence of delamination during and after fracture toughness tests of API X80 steel plates. Strength of Materials. IntechOpen. London. UK. 2020. Chapter 3. pp. 1–26.
21. Stolheim D. D. Modern alloying schemes and practices in production of high-strength steels for main oil pipelines. Part 1. Metallurg. 2013. No. 11. pp. 53–67.
22. Gómez M., Rancel L., Gómez P. P., Robla J. I. et al. Simplification of hot rolling schedule in Ti-microalloyed steels with optimized Ti/N ratio. ISIJ Int. 2010. Vol. 50, Iss. 6. pp. 868–874.
23. Wang S., Gao Z., Wu G. et al. Titanium microalloying of steel: A review of its effects on processing, microstructure and mechanical properties. Int. J. Miner. Metall. Mater. 2022. Vol. 29. pp. 645–661.
24. Naumenko V. V., Muntin A. V., Chervonnyi A. V., Efron L. I. Effect of microalloying on the microstructure and level of mechanical properties of K56 strength class coil rolled products produced under casting and rolling complex conditions. Stal. 2015. No. 7. pp. 50–56.
25. Chervonnyi A. V., Naumenko V. V., Muntin A. V., Efron L. I. et al. Microalloying of cold-resistant pipe steels for production of rolled products at a casting and rolling complex. Stal. 2015. No. 9. pp. 56–61. |