ArticleName Structure and properties of SV-AK5 alloy during pulse-arc surfacing
DOI 10.17580/tsm.2023.11.10
ArticleAuthor Dunaev D. A., Zhatkin S. S., Nikitin K. V., Minakov E. A.
ArticleAuthorData

Samara State Technical University, Samara, Russia

D. A. Dunaev, Engineer at the Department of Casting and High-Performance Technology, Postgraduate Student, e-mail: dimjkee830@gmail.com
S. S. Zhatkin, Professor at the Department of Casting and High-Performance Technology, Candidate of Technical Science, e-mail: sergejat@mail.ru
K. V. Nikitin, Professor at the Department of Casting and High-Performance Technology, Dean of the Faculty of Mechanical Engineering, Metallurgy and Transport, Doctor of Technical Science, e-mail: kvn-6411@mail.ru
E. A. Minakov, Assistant Lecturer at the Department of Casting and High-Performance Technology, Engineer, e-mail: goodspik@yandex.ru

Abstract

This paper describes the results of a study that looked at the structure and properties of arc additive manufactured Al – Si alloy. The surfacing was performed using Sv-Ak5 wire in standard pulse mode and in coldArc mode in an upgraded 3D printer. The arc currents of 60, 70 and 75 А were applied. The authors looked at how the different surfacing modes influenced the dimensions, microstructure, gas porosity and mechanical properties of surfaced specimens. It was found that in both modes the rising current strength leads to increased dimensions of a specimen. The surfacing width becomes bigger due to melt spreading. In the сoldArc mode such deviations are smaller. As the current strength rises, the cooling rate drops leading to larger sizes of α-Al dendrites. Maximum sizes of dendrites are typical of the middle zones of the built-up layer, whereas minimum size dendrites can be found in the bottom zones. This can be attributed to the fact that when building the first layer heat dissipates mainly through the substrate thus ensuring high cooling rates. At the same time, the middle layer is built when the heat dissipation and cooling rates are lower, which explains the larger α-Al sizes. It was also established that smaller dendrites are formed in the layer structure in the сoldArc mode compared with the standard pulse mode. A rise in the arc current to 75 A leads to a reduced cooling rate making the liquid phase stay longer. This explains a risen concentration of gas pores per unit area. The highest concentration of gas pores can be found in the middle zones of surfaced specimens. When applying either the standard pulse mode or the сoldArc mode, the surfaced specimens manifest almost identical mechanical properties.
Support for this research was provided by the Russian Science Foundation under Project No. 23-29-10195.

keywords Additive manufacturing, arc surfacing, fillers, structure, mechanical properties
References

1. Ngo T. D., Kashani Alireza, Imbalzano Gabriele, Nguyen K. T. Q. et al. Additive manufacturing (3D printing): a review of materials, methods, applications and challenges. Composites Part B: Engineering. 2018. Vol. 143. pp. 172–196.
2. Lindgren L.-E., Lundbaeck A. Approaches in computational welding mechanics applied to additive manufacturing: Review and outlook. Comptes Rendus Mecanique. 2018. Vol. 346, Iss. 11. pp. 1033–1042.
3. Gu J., Wang X., Bai J., Ding J. et al. Deformation microstructures and strengthening mechanisms for the wire + arc additively manufactured Al – Mg4.5Mn alloy with inter-layer rolling. Materials Science & Engineering A. 2018. Vol. 712. pp. 292–301.
4. Liberini М., Astarita А., Campatelli G., Scippa A. et al. Selection of optimal process parameters for wire arc additive manufacturing. Procedia CIRP. 2017. Vol. 62. pp. 470–474.
5. Herzog D., Seyda V., Wycisk E., Emmelmann C. Additive manufacturing of metals. Acta Materialia. 2016. Vol. 117. pp. 371–392.
6. Wang F., Williams S., Colegrove P., Antonysamy A. Microstructure and mechanical properties of wire and arc additive manufactured Ti – 6A1 – 4V. Metallurgical and Materials Transactions A. 2013. Vol. 44. pp. 968–977.
7. Ding D., Pan Z., Cuiuri D., Li H. Wire-feed additive manufacturing of metal components: technologies, developments and future interests. International Journal of Advanced Manufacturing Technology. 2015. Vol. 81, Iss. 1-4. pp. 465–481.
8. Köhler M., Fiebig S., Hensel J., Dilger K. Wire and arc additive manufacturing of aluminum components. Metals. 2019. Vol. 9, No. 5. pp. 1–9.
9. Köhler M., Hensel J., Dilger K. Effects of thermal cycling on wire and arc additive manufacturing of Al-5356 components. Metals. 2020. Vol. 10, No. 7. pp. 2–11.
10. Jandric Z., Labudovic M., Kovacevic R. Effect of heat sink on microstructure of three-dimensional parts built by welding-based deposition. International Journal of Machine Tools and Manufacture. 2004. Vol. 44, Iss. 7-8. pp. 785–796.
11. Kostin V. A., Grigorenko G. M. Modelling the process of building a multi-layer 3D surface by additive technology using welding heat sources. Tekhnologiya mashinostroeniya. 2019. No. 7. pp. 39–51.
12. Shapovalov V. A., Grigorenko G. M. Control over the metal structure during crystallization. Sovremennaya elektrometallurgiya. 2015. No. 2. pp. 51–54.

13. Kou S. Welding metallurgy. New Jersey : John Wiley & Sons, Inc, 2003. 480 p.
14. Fang X., Zhang L., Li H., Li С. et al. Microstructure evolution and mechanical behavior of 2219 aluminum alloys additively fabricated by the cold metal transfer process. Materials. 2018. Vol. 11, No. 5. pp. 812–824.
15. Köhler M., Fiebig S., Hensel J., Dilger K. Wire and arc additive manufacturing of aluminum components. Metals. 2019. Vol. 9, No. 5. pp. 1–9.
16. Ayarkwa K., Williams S., Ding J. Investigation of pulse advance cold metal transfer on aluminium wire arc additive manufacturing. International Journal of Rapid Manufacturing. 2015. Vol. 5, No. 1. pp. 44–57.
17. Zhang Ch., Li Yu., Gao M., Zeng X. Wire arc additive manufacturing of Al – 6Mg alloy using variable polarity cold metal transfer arc as power source. Materials Science & Engineering A. 2018. Vol. 711. pp. 415–423.
18. Baoqiang C., Jialuo D. Effect of arc mode in cold metal transfer process on porosity of additively manufactured Al – 6.3% Cu alloy. International Journal of Advanced Manufacturing Technology. 2015. Vol. 76, Iss. 9-12. pp. 1593–1606.
19. Horgar А., Fostervoll Н., Nyhus B., Ren X. et al. Additive manufacturing using WAAM with AA5183 wire. Journal of Materials Processing Technology. 2018. Vol. 259. pp. 68–74.
20. Wang Y., Yang S., Xie C., Liu H. et al. Microstructure and ratcheting behavior of additive manufactured 4043 aluminum alloy. Journal of Materials Engineering and Performance. 2018. Vol. 27, Iss. 3. pp. 4582–4592.
21. Salomatova E. S., Kartashev M. F., Trushnikov D. N., Permyakov G. L. et al. Understanding the processes behind evaporation of alloying components during CMT surfacing of AlMg5 type wire. Izvestiya TulGU. Tekhnicheskie nauki. 2019. Iss. 10. pp. 305–311.
22. Rauch M., Nwankpa U. V., Hascoet J.-Y. Investigation of deposition strategy on wire and arc additive manufacturing of aluminium components. Journal of Advanced Joining Processes. 2021. Vol. 4. pp. 1–8.
23. Qi Z., Cong B, Qi B., Sun H. et al. Microstructure and mechanical properties of double-wire + arc additively manufactured Al – Cu – Mg alloys. Journal of Materials Processing Technology. 2018. Vol. 255. pp. 347–353.
24. Henckell Ph., Gierth M., Ali Y., Reimann J. et al. Reduction of energy input in wire arc additive manufacturing (WAAM) with gas metal arc welding (GMAW). Materials. 2020. Vol. 13, Iss. 11. 2491.
25. de Dompablo M. New solutions in coldArc and forceArc welding technology. Welding International. 2011. Vol. 27, No. 1. pp. 1–6.
26. Panchenko O. V., Zhabrev L. A., Kurushkin D. V., Popovich A. A. Macrostructure and mechanical properties of Al – Si, Al – Mg – Si, and Al – Mg – Mn aluminum alloys produced by electric arc additive growth. Metal Science and Heat Treatment. 2019. Vol. 60, No. 11–12. pp. 749–754.
27. GOST 7871–2019. Filler wire of aluminium and aluminium alloys. Specifications. Introduced: 01.02.2020.
28. Nerovnyi V. M., Konovalov A. V., Yakushin B. F., Makarov E. L. et al. Theory of welding processes (2nd edition). Moscow : MGTU im. N. E. Baumana, 2016. 704 p.
29. GOST 1497–84. Metals. Methods of tension test. Introduced: 01.01.1986.
30. GOST 10006–80. Metal tubes. Tensile test method. Introduced: 01.07.1980.

Language of full-text russian
Full content Buy
Back