Production of quality NiAl granules: examining process features |
| Abstract |
This paper looks at a number of different methods for producing nickel aluminide (NiAl) granules. It also examines certain factors hindering a wider application of the above material by current aircraft and engine makers. The key hindering factors that were established include an almost zero plasticity of the material under pressure forming and a poor machinability of parts made of it. Application of precise metallurgy techniques, which help obtain almost finished parts requiring minimum machining, can help eliminate the above factors. Another difficulty is related to the fact that there are no techniques that can help obtain quality ball-shaped granules using the material in view. The conducted study helped define some quality criteria applicable to the resulting granules. They include sphericity, size consistency, absence of defects such as pores or surface satellites, presence of fine-dispersed dendritic structure, etc. A number of methods was considered that enable to produce high-quality nickel aluminide granules, such as high-temperature inert gas jet atomization; Plasma Rotary Electrode Process (or, PREP); meltspinning with the help of perforated crucible. It was established that PREP delivers the optimum technique for obtaining quality NiAl granules. In the course of the study it was established that it is not that much the current I but rather the velocity of the melted electrode n that serves as the key characteristic of the process that determines the quality and diameter of granules, as well as the dendritic parameter of their microstructure. Optimal electrode RPM values were determined. They are n ≈ 15 000–16 000 min–1 at the current I ≈ 1.000–1.500 A. A process has been developed for producing quality NiAl granules, which involves the following stages: self-propagating high-temperature synthesis to make initial NiAl ingots followed by remelting, heat treatment, granule separation and PREP. |
| References |
1. Bochenek K., Basista M. Advances in processing of NiAl intermetallic alloys and composites for high temperature aerospace applications. Progress in Aerospace Sciences. 2015. Vol. 79. pp. 136–146.
2. Buntushkin V. P., Bazyleva O. A., Burkina V. I. High-temperature heatresistant Ni3Al alloys for gas-turbine engine hot section parts. Aviatsionnaya promyshlennos. 2007. No. 2. pp. 41–43.
3. Reed R. C. The superalloys fundamentals and applications. UK, Cambridge : Cambridge University Press, 2006. 372 p.
4. Dey G. K. Physical metallurgy of nickel aluminides. Sadhana. 2003. Vol. 28. pp. 247–262.
5. Kablov E. N., Buntushkin V. P., Bazyleva O. A. Structural heat-resistant Ni3Al-based materials for gas-turbine engine hot section parts. Tekhnologiya legkikh splavov. 2007. No. 2. pp. 75–80.
6. Xu G. H., Zhang K. F., Huang Z. Q. The synthesis and characterization of ultrafine grain NiAl intermetallic. Advanced Powder Technology. 2012. Vol. 23. pp. 366–371.
7. Povarova K. B., Drozdov A. A., Skachkov O. A., Morozov A. E. Physicochemical approaches to designing NiAl-based alloys suitable for high-temperature duty. Metally. 2011. No. 2. pp. 48–62.
8. Sentyurina Zh. A. Use of NiAl-based alloys to produce globular powders for additive manufacturing: dissertation Candidate of Technical Sciences. Moscow : MISIS, 2016. 168 p.
9. Shevtsova L. I. The structure and mechanical properties of nickel aluminide materials produced by spark plasma sintering of powder mixtures: dissertation Candidate of Technical Sciences. Novosibirsk : NGTU, 2015. 198 p.
10. Angelo P. C., Subramanian R. Powder metallurgy: science, technology and applications. Delhi : PHI Learning Pvt. Ltd., 2008. 312 p.
11. Bojarevics V., Roy A., Pericleous K. Numerical model of electrode induction melting for gas atomization. The International Journal for Computation and Mathematics in Electrical and Electronic Engineering. 2011. Vol. 30, Iss. 5. pp. 1455–1466.
12. Xia Y., Khezzar L., Alshehhi M., Hardalupas Y. Droplet size and velocity characteristics of water-air impinging jet atomizer. International Journal of Multiphase Flow. 2017. Vol. 94. pp. 31–43.
13. Ario Sunar Baskoro, Sugeng Supriadi Dharmanto. Review on plasma atomizer technology for metal powder. MATEC Web of Conferences. 2019. Vol. 269. 05004. DOI: 10.1051/matecconf/ 201926905004.
14. Samal S. Thermal plasma technology: the prospective future in material processing. Journal of Cleaner Production. 2017. Vol. 142. pp. 3131–3150.
15. Galkin E. V., Zharov M. V. The prospective technology of production of metal materials grains with extra high rate of solidification. IOP Conference Series: Materials Science and Engineering. 17th International School-Conference “New Materials: Advanced Technologies”. 2020. 012020.
16. Zharov M. V. Understanding the properties of pressed Al – Cu – Mg materials made of granules obtained by meltspinning. Tekhnologiya Mashinostroeniya. 2021. No. 4. pp. 5–9.
17. Zharov M. V. Investigation of the features of crystallization of granules of high-strength aluminum alloys of the Al – Zn – Mg – Cu system at ultra-high cooling rates. PNRPU Mechanics Bulletin. 2021. No. 4. pp. 71–82.
18. TU 6-09-4272–84. Reagents, pure chromium (III) oxide (dichromium trioxide), pure for analysis. Specifications. Introduced: 01.01.1985.
19. TU 48-4-176–85. Hafnium powder. Introduced: 01.01.1986.
20. GOST 6058–73. Aluminium powder. Specifications. Introduced: 01.01.1975.
21. GOST 20899–98. Metallic powders. Determination of flowability by means of a calibrated funnel (Hall flowmeter). Introduced: 01.07.2001.
22. GOST 19440–94. Metallic powders. Determination of apparent density. Introduced: 01.01.1997.
23. GOST 19440–94. Metallic powders. Determination of tap density. Introduced: 01.01.1997.
24. Zhu H., Tong H., Yang F., Cheng C. Plasma-assisted preparation and characterization of spherical stainless steel powders. Journal of Materials Processing Technology. 2018. Vol. 252. pp. 559–566.
25. Mohanty T., Tripathi B., Mahata T., Sinha P. Arc plasma assisted rotating electrode process for preparation of metal pebbles. Discharges and Electrical Insulation in Vacuum (ISDEIV). International Symposium. 2014. pp. 741–744.
26. Entezarian M., Allaire F., Tsantrizos P., Drew R. A. Plasma atomization: a new process for the production of fine, spherical powders. The Journal of the Minerals, Metals & Materials Society. 1996. Vol. 48. pp. 53–55.
27. Teleshov V. V. The fundamental trend of a changing structure during crystallization of aluminium alloys at different cooling rates. Tekhnologiya legkikh splavov. 2015. No. 2. pp. 13–18.
28. Xu G. N., Zhang K. F., Huang Z. Q. The synthesis and characterization of ultrafine grain NiAl intermetallic. Advanced Powder Technology. 2012. Vol. 23. pp. 366–371.
29. M. B. Silin, M. V. Zharov. Method of producing metal granules. Patent RF, No. 2117556. Published : 20.08.1998. |