MMC Norilsk Nickel’s Polar Division, Norilsk, Russia:

A. D. Borodin, Category I Process Engineer at the Engineering Support Centre, e-mail: borodinad@nornik.ru
P. V. Malakhov, Principal Specialist at the Science and Technology Directorate, e-mail: malakhovpv@nornik.ru
V. G. Orudzhov, Category I Process Engineer at the Engineering Support Centre, e-mail: orudzhovvg@nornik.ru
S. I. Chipilyaga, Chief Engineer at the Smelting Shop of the Copper Plant, e-mail: chipilyagasi@nornik.ru

At the final stage of the anode copper production process adopted by the Copper Plant of MMC Norilsk Nickel’s Polar Division, anode copper is poured in the moulds, the melt and the moulds are cooled down by process water spraying, the anodes are pushed out of the moulds and moved into accumulator bathes for final cooling with running water. The same anode copper is used to make moulds by casting, which ensures a waste-free production circuit and saves the need to use moulds made of other materials in the Norilsk Industrial Area. Parting compounds are used to prevent penetration of anodes. They are refractory powders proportionally blended with process water or alcohol that are poured, sprayed or brushed over the working surface of the mould and let to dry. Two drawbacks can be pointed out with regard to the parting compounds that are used by the Copper Plant. These drawbacks were observed during the casting process. A thinner layer of anode copper is formed with each casting cycle leading to penetration, surface defects or surface warping. Such anodes are rejected. Besides, as a result of being constantly in contact with the melt, the mould surface start to crack as it wears out. During casting and cooling, particles separate from the parting compound and transfer to the surface of the copper anode. Cool anodes are moved to the Copper Electrowinning Section to be placed in the electrolysis bathes, where the parting compound particles, insoluble in sulphuric acid solutions, form an electrolytic slime. The insoluble particles contain oxides of silicon, aluminium, magnesium, calcium, etc. These impurities make slime harder to process in the Metallurgical Shop affecting the quality of the final product – i.e. platinum group metal concentrate. This research aims to identify possibilities to improve the surface quality of anodes and reduce penetration so that less components of the parting compound reached the Copper Electrowinning Section or the Metallurgical Shop. In the course of this research, the optimum size distribution of the parting compound was identified; the conditions are described in which the parting compound is used at the Copper Plant; laboratory and pilot tests were conducted with an experimental parting compound that is not normally used by the Copper Plant in the copper anode production circuit.

1. Kazantsev S. P., Furman E. L. Defects typical of investment casting: Educational e-resource. Yekaterinburg : UrFU, 2019. 110 p.
2. Xi Zhao, Shuo Xu, Jing Liu. Surface tension of liquid metal: role, mechanism and application. Frontiers in Energy. 2017. Vol. 11. pp. 535–567.
3. Gelfman M. I., Kovalevich O. V., Yustratov V. P. Colloid chemistry: Textbook for university students. 7th reprint edition. Saint Petersburg : Lan, 2020. 336 p.
4. Rubarsk J., Bialy W. Spreading of cracks due to thermal fatigue in metal molds. Multidisciplinary Aspects of Production Engineering. 2018. Vol. 1, Iss. 1. pp. 11–18.
5. Yanyushkin Yu. M. Thermo-physical and performance properties of refractory and insulation materials: Learner’s guide. Moscow : Izdatelskiy Dom MISiS, 2014. 91 p.
6. Announcement LPiS-10-2000. Optimization of copper anode casting process to ensure three unloads during electrorefining. Norilsk : GMOITs ZF OAO “NGK”, 2000. 30 p.
7. Vdovin K. N., Pivovarova K. G., Ponomareva T. B., Feoklistov N. A. Optimized composition of the parting compound used in steel casting. Liteyshchik Rossii. 2018. No. 6. pp. 14–17.
8. Kovaleva T. V., Isagulov A. Z. Parting compound thickness and its effect on the casting quality in lost-foam casting. Proceedings of the 19^th International Conference Kulagin Readings: Manufacturing Equipment and Processes. 2019. pp. 203–208.
9. Anawar Md. H.; Strezov V. et al. Sustainable and economic waste management : resource recovery techniques. New York : CRC Press, Taylor & Francis Group, 2020. 316 p.
10. Seisco S., Aromaa J., Latostenmaa O., Forsen O., Wilson B. et al. Pressure leaching of decopperized copper electrorefining anode slimes in strong acid solution. Physicochemical Problems of Mineral Processing. 2017. Vol. 53, Iss. 1. pp. 465–474.
11. Mubarok Z., Filzwieser I., Paschen P. Dendritic Cathode Growth during Copper Electrorefining in the Presence of Solid Particles. Erzmetall. 2005. Vol. 58, No. 6. p. 315.
12. Ozerov S. S., Portov A. B., Tsymbulov L. B., Mashyanov A. K. Assessment of efficiency of using the polyvinyl alcohols as binder during the briquetting of flotation copper-nickel concentrate. Tsvetnye Metally. 2016. No. 8. pp. 39–45. DOI: 10.17580/tsm.2016.08.05.
13. GOST 10772–78. Water foundry coatings for mould paints. General specifications. Introduced: 01.01.1979.