Formation of hot cracks on continuously cast round billets is the frequent problem in metallurgical production. The article presents the results of a study of the macrostructure, surface quality and technology of continuous casting of round billets with a diameter of 455 mm, produced at the bloom caster of Ural Steel JSC. The main defects of such billets are identified as surface cracks of “combined” type, namely, transverse cracks (the share among the billets with defects is 9.1%), cracks of the mesh form (the share among the billets with defects is 8.3%). The main reasons for the unsatisfactory quality of the ingot are determined: increased overheating of metal in the tundish, which can be partially compensated by reduction of the casting speed, and intensive cooling of billet surface in the first segments of secondary cooling, which increase thermal stresses in metal with consequent heating of surface layers. It was decided that the most effective way to minimize billet defects is to improve the secondary cooling technology in compliance with the regulated casting temperature and speed procedure. Thermal calculations of billet solidification are conducted. It was revealed that overcooling of billet surface occurs in the first segments of secondary cooling under the existing secondary cooling modes and temperature and speed modes of casting, which leads to additional thermal and phase stresses. In the third segment of the secondary cooling zone, heating of the billet surface is observed due to the heat of the central part. Rational flow rates of cooling agent for the secondary cooling segments of the bloom continuous casting machine are proposed. They include expansion of the active section of secondary cooling with a reduction of cooling agent consumption in the first segments will reduce the thermal cycling processes in the hardened crust and minimize the likelihood of cracking.

The work was conducted under financial support of the RF Ministry of Science and High Education (project No. FZRU-2020-0011).

1. Brovman M. Ya. Continuous casting of metals. Moscow. EKOMET. 2007. 484 p.
2. Parshin V. M., Bulanov L. V. Continuous casting of steel. Lipetsk. “NLMK” JSC. 2011. 221 p.
3. Smirnov A. N., Kuberskiy S. V., Shtepan E. V. Continuous casting of steel: a manual. Donetsk. DonNTU. 2011. 482 p.
4. Flesch R., Bleck W. Crack susceptibility of medium and high alloyed tool steels under continuous casting conditions. Steel Research. 1998. Vol. 69. No. 7. pp. 292–299.
5. Alvarez de Toledo G., Arteaga A., Laraudogoitia J. J. Continuous Casting of Microalloyed Steels. Influence of Composition and Operational Parameters in Billet Surface Cracking. Materials Science Forum. 2005. Vol. 500–501. pp. 163–170.
6. Zhang J. et al. Effects of an even secondary cooling mode on the temperature and stress fields of round billet continuous casting steel. Journal of Materials Processing Technology. 2015. Vol. 222. pp. 315–326.
7. Fan H., Long M., Yu S. et al. Uniform Secondary Cooling Pattern for Minimizing Surface Reheating of the Strand During Round Bloom Continuous Casting. Journal of Minerals, Metals & Materials Society (JOM). 2018. Vol. 70. pp. 237–242.
8. Wang R., Bao Y.-P., Li Y.-H., An H.-H. Optimization of secondary cooling in continuous casting of round billet. Metallurgical Research and Technology. 2015. Vol. 112. p. 302.
9. Long M., Dong Z., Sheng J., Chen D., Chen C. Universal Secondary Cooling Structure for Round Blooms Continuous Casting of Steels in Various Diameters. Steel Research International. 2015. Vol. 86. No. 2. pp. 154–162.
10. Chen W., Zhang Y.-Z., Zhang C.-J., Zhu L.-G., Wang S.-M., Wang B.-X., Ma J.-H., Lu W.-G. Thermomechanical analysis and optimisation for beam blank continuous casting. Ironmaking & Steelmaking. 2008. Vol. 35. No. 2. pp. 129–136.
11. Chen W., Zhang Y.-Z., Wang B.-X. Optimisation of continuous casting process parameters based on coupled heat and stress model. Ironmaking & Steelmaking. 2010. Vol. 37. No. 2. pp. 147–154.
12. Long M.J., Chen D.F., Zhang J., Ouyang Q. Novel online temperature control system with closed feedback loop for steel continuous casting. Ironmaking & Steelmaking. 2013. Vol. 38. No. 8. pp. 620–629.
13. Wang X., Wang Z., Liu Y., Du F., Yao M., Zhang X. A particle swarm approach for optimization of secondary cooling process in slab continuous casting. International Journal of Heat and Mass Transfer. 2016. Vol. 93. pp. 250–256.
14. Chakraborti N., Gupta R. S. P., Tiwari T. K. Optimisation of continuous casting process using genetic algorithms: studies of spray and radiation cooling regions. Ironmaking & Steelmaking. 2003. Vol. 30. No. 4. pp. 273–278.
15. Ji C., Cai Z. Z., Wang W. L., Zhu M. Y., Sahai Y. Effect of transverse distribution of secondary cooling water on corner cracks in wide thick slab continuous casting process. Ironmaking & Steelmaking. 2014. Vol. 41. No. 5. pp. 360–368.
16. Sun H., Li L. Formation and control of macrosegregation for round bloom continuous casting. Ironmaking & Steelmaking. 2015. Vol. 42. No. 9. pp. 683–688.
17. Luo W., Yan B., Xiong Y. X., Wen G. H., Xu H. L. Improvement to secondary cooling scheme for beam blank continuous casting. Ironmaking & Steelmaking. 2012. Vol. 39. No. 2. pp. 125–132.
18. Zong N., Zhang H., Liu Y., Lu Zh. Analysis on morphology and stress concentration in continuous casting bloom to learn the formation and propagation of internal cracks induced by soft reduction technology. Ironmaking & Steelmaking. 2019. Vol. 46. No. 9. pp. 872–885.
19. Pan H. Control Technology of Internal Quality for CC Billet. Advanced Materials Research. 2012. Vol. 415-417. pp. 1729–1734.
20. Zhang L.W., Wang Z. L., Xu C. J. et al. A vertical continuous casting machine for large blooms. Ironmaking & Steelmaking. 2019. Vol. 46. No. 8. pp.742–746.
21. Barna M., Javurek M., Reiter J. et al. Numerical Simulations of Mould Electromagnetic Stirring for Round Bloom Strands. Bergische und Huettenmaennische Monatshefte. 2009. Vol. 154. p. 518.
22. Rauter W., Reiter J., Srienc K. et al. Soft Reduction at a Round Bloom Caster: Implementation and Results. Bergische und Huettenmaennische Monatshefte. 2014. Vol. 159. pp. 454–460.
23. Tutarova V. D., Safonov D. S., Shapovalov A. N. Density distribution of the spray from flat spray nozzles in the secondary-cooling zone of a continuous caster. Metallurgist. 2012. Vol. 56. No. 5–6. pp. 438–442.
24. Shevchenko E. A., Stolyarov A. M., Shapovalov A. N., Baranchikov K. V. Transverse distortion of continuous-cast slab. Steel in Translation. 2014. Vol. 44. No. 1. pp. 17–20.
25. Shevchenko E. A., Stolyarov A. M., Shapovalov A. N., Baranchikov K. V. Preventing convexity at the narrow faces of continuouscast billet. Steel in Translation. 2015. Vol. 1. pp. 29–32.
26. Kalitaev A. N., Tutarova V. D., Shapovalov A. N. Effect of Continuous Casting Parameters on Quality of Billets Manufactured by UMMC Steel LLC. Solid State Phenomena. 2017. Vol. 265. pp. 952–961.
27. Kasyan G. I., Pisarskiy S. N., Sirchenko V. I. Experience of mastering and improvement of production technology for round section billets at the continuous casting machine in the electric steel melting shop of the Mini-metallurgical plant “ISTIL” (Ukraine). Metall i lityo Ukrainy. 2009. No. 3. pp. 6–9.