ArticleName |
Thermal decomposition of synthetic aluminium hydroxide with different degrees of dispersion |
ArticleAuthorData |
Chelyabinsk State University, Chelyabinsk, Russia:
A. V. Tolchev, Head of the Department of Chemical Technology and Computational Chemistry, Doctor of Chemiсal Sciences, Professor, e-mail: avtolchev@csu.ru A. P. Tronov, Senior Lecturer at the Department of Chemical Technology and Computational Chemistry, e-mail: arteq_tron@mail.ru |
Abstract |
Using such analysis techniques as X-ray analysis, electron scanning microscopy and isothermal and non-isothermal analysis, the authors examined the structure of particles in synthetic aluminium hydroxide with different degrees of dispersion, as well as the composition and structure of the products of their thermolysis in order to identify factors contributing to the formation of a γ-modification of aluminium oxohydroxide in the process of thermal decomposition of γ-Al(OH)3. The study focused on synthetic aluminium hydroxide produced by the Urals Aluminium Smelter (gibbsite). The material was screened into two size fractions: coarse material — with the particles bigger than 200 μm, and fine material — with the particles <20 μm. The initial particles of aluminium hydroxide studied with the help of electron scanning microscopy can be characterized with a block structure, and they consist of smaller crystals, the sizes and the shapes of which may differ depending on the initial particle size distribution. Electron microscopy and X-ray studies showed that the coarse particles of aluminium hydroxide consist of imperfect little plate-like crystals with the form factor of 30–50. The fine particles of γ-Аl(ОН)3 are mainly comprised of formations that contain a few or dozens of little prismatic crystals or, which is more rare, individual little prismatic crystals. Through experiments it was established that thermolysis of γ-Аl(ОН)3 with the particles bigger than 200 μm resulted in a greater amount of aluminium oxohydroxide with the structure of boehmite (approximately by 25%) formed compared with thermolysis of fine particles with the size <20 μm. It is demonstrated that the main differentiating characteristics of the coarse particles of aluminium hydroxide include imperfections and the platelike shape of the crystals which build the particles of the coarse-disperse γ-Аl(ОН)3. The authors suggest that they are the above differentiating characteristics that cause microstresses in the crystals, which increase the reactivity of aluminium hydroxide and, under otherwise equal conditions, help the formation of the γ-AlOOH phase. |
References |
1. Nikolskaya M. P., Kuznetsova E. V. Production of alumina from bauxites. Kamensk-Uralsky, 2007. 184 p. 2. Godovikov A. A. Mineralogy. 2nd revised edition. Moscow : Nedra, 1983. 647 p. 3. Digne M., Sautet P., Raybaud P., Toulhoat H., Artacho E. Structure and stability of hydroxides: a theoretical study. Journal of Physical Chemistry B. 2002. Vol. 106. pp. 5155–5162. 4. Candela L., Perlmutter D. D. Kinetics of boehmite formation by thermal decomposition of gibbsite. Industrial and Engineering Chemistry Research. 1992. Vol. 31, No. 3. pp. 694–700. 5. Chen B., Xu X., Chen X., Kong L., Chen D. Transformation behavior of gibbsite to boehmite by steam-assisted synthesis. Journal of Solid State Chemistry. 2018. Vol. 265. pp. 237–243. 6. Filho R.W., Rocha G. A., Montes C. R., Vieira-Coelho A. C. Synthesis and characterization of boehmites obtained from gibbsite in presence of different environments. Materials Research. 2016. Vol. 19, No. 3. pp. 659–668. 7. Danilevich V. V., Klimov O. V., Nadeina K. A., Gerasimov E. Yu., Cherepanova S. V., Vatutina Yu. V., Noskov A. S. Novel eco-friendly method for preparation of mesoporous alumina from the product of rapid thermal treatment of gibbsite. Superlattices and Microstructures. 2018. Vol. 120. pp. 148–160. 8. Sulaiman Y. M., Takip K. M., Sapiee N. A., Zahari A. K. Synthesis of Aluminium Hydroxide and Alumina by Hydrothermal and Solvothermal Methods. Materials Science Forum. 2016. Vol. 840. pp. 359–363. 9. Redaoui D., Sahnoune F., Heraiz M., Raghdi A. Mechanism and kinetic parameters of the thermal decomposition of gibbsite Al(OH)3 by thermogravimetric analysis. Acta Physica Polonica: A. 2017. Vol. 131, No. 3. pp. 562–565. 10. Kuznetsov S. I. The growth of hydrargillite crystals in the process of aluminium solution decomposition. Tsvetnye Metally. 1956. No. 11. pp. 59–63. 11. Chistyakova A. A., Kavina V. A. Understanding the transformations of aluminium hydroxides in alkaline-aluminate solutions. Tsvetnye Metally. 1963. No. 11. pp. 46–53. 12. Arakelyan O. I., Pavlov Yu. I., Tsvetkova M. V. et al. Effect of the microstructure of aluminium hydroxide on the quality of alumina and determining the size distribution of aluminium hydroxide using microscope. Proizvodstvo glinozema. Trudy VAMI. 1976. No. 94. pp. 96–101. 13. Volokhov Yu. A., Teslya V. G., Anisimova G. V. et al. Formation of secondary crystals of aluminium hydroxide in aluminate solutions. Tsvetnye Metally. 1989. No. 3. pp. 63–66. 14. Brichkin V. N., Sizyakova E. V. The growth and morphology of commercial aluminium hydroxide. Tsvetnye Metally. 2006. No. 9. pp. 62–65. 15. Sweegers C., de Coninck H. C., Meekes H. et al. Morphology, evolution and other characteristics of gibbsite crystals grown from pure and impure aqueous sodium aluminate solutions. Journal of Crystal Growth. 2001. Vol. 233, No. 3. pp. 567–582. 16. Sawsan J. F., Parkinson G. M. Surface morphology and crystal growth mechanism of gibbsite in industrial Bayer liquors. Hydrometallurgy. 2005. Vol. 78, No. 3. pp. 246–255. 17. Sawsan J. F., Parkinson G. M., Reyhani M. M. Direct observation of the growth of gibbsite crystals by atomic force microscopy. Journal of Crystal Growth. 2004. Vol. 260. pp. 232–242. 18. Brown N. Crystal growth and nucleation of aluminium trihydroxide from seeded caustic aluminate solutions. Journal of Crystal Growth. 1972. Vol. 12, No. 11. pp. 39–45. 19. Sawsan J. F., Parkinson G. M., Reyhani M. M. Atomic force microscopy study of the growth mechanism of gibbsite crystals. Physical Chemistry Chemical Physics. 2004. No. 6. pp. 1049–1055. 20. Misra C., White E. T. Crystallisation of Bayer aluminium trihydroxide. Journal of Crystal Growth. 1971. Vol. 8, No. 2. pp. 172–178. 21. Tolchev A. V., Kazantseva E. L., Larin D. D. Investigation of gibbsite structure with various dispersion degree. Tsvetnye Metally. 2010. No. 1. pp. 57–59. 22. Tolchev A. V. Phase and structural transformations of aluminium compounds with different degrees of dispersion. Chelyabinsk Physical and Mathematical Journal. 2011. No. 39. pp. 24–29. 23. Encyclopedia of chemistry. In 5 volumes. Moscow : Sovetskaya entsiklopediya, 1983. Vol. 1. 623 p. 24. Kalinina A. M. On the relationship between the structure and thermal transformations in various compounds formed by aluminium oxide. Chemistry and technology of alumina: Proceedings of the 4th All-Soviet Union Meeting. Novosibirsk : Sibirskoe otdelenie izdatelstva Nauka, 1971. pp. 360–369. |