Journals →  Non-ferrous Мetals →  2017 →  #2 →  Back

MATERIAL SCIENCE
ArticleName Analysis of the phase composition and microstructure of a TNM-type alloy by using thermodynamic calculation
DOI 10.17580/nfm.2017.02.08
ArticleAuthor Akopyan T. K., Korotkova N. O., Dolbachev A. P.
ArticleAuthorData

National University of Science and Technology MISiS, Moscow, Russia:
N. O. Korotkova, Post-Graduate Student of the Department of Metal Forming
A. P. Dolbachev, Engineer of the Department of Metal Forming

 

1National University of Science and Technology MISiS, Moscow, Russia ; 2Baikov Institute of Metallurgy and Materials Science, Moscow, Russia.

T. K. Akopyan, Research Fellow of the Department of Metal Forming1,2, e-mail: nemiroffandtor@yandex.ru

Abstract

Using both thermodynamic calculations and experimental analyses, the phase composition and microstructure of the new TNM-type alloy with the following actual compositions, % (at.): TNM – 40.05 Al, 4.51 Nb and 1.05 Mo have been analysed. According to thermodynamic calculation, equilibrium solidification of the new alloy proceeded via the β-phase, i. e. L → L + β → β, followed by the solid-state transformations, the main of which is the eutectoid reaction α → α2 + β + γ. The microstructure of the alloy in the as-cast state and after high-temperature vacuum annealing was examined by means of scanning electron microscopy and electron microprobe analysis. Experimental studies have shown that the main structural component is the lamellar γ/α2-colonies (with a thickness of individual plates of about 300 nm) surrounded by the β- and γ-phase crystals, the total fraction of which does not exceed 30% (vol.). According to the electron microprobe analysis, β-phase contains the largest amount of molybdenum, while the concentration of aluminium is the smallest. In contrast, the γ/α2-colonies (initial α-phase) and γ-phase have higher aluminium and minimum molybdenum content. The observed results are in a good agreement with the results of the thermodynamic calculation. Experimental quantitative analysis of the phase fraction after vacuum annealing at 1250 oC of the new alloy has revealed that the total amount of -phase does not exceed 8% (vol.), what practically corresponds to the base TNM (Ti43.5Al4Nb1Mo) alloy after similar heat treatment. However, the base alloy also contains up to 14% of the γ-phase, which is not observed in the new alloy. After annealing at 1100 oC, new alloy contains up to 24% (vol.) β-phase and 4% (vol.) γ-phase, while the base TNM alloy contains up to 14% (vol.) β-phase and 21% (vol.) γ-phase. In general, we can conclude that a reduction of aluminum content from 43.5 to 40.0% (at.) leads to a considerable increase in the amount of β-phase and decrease the γ-phase content. It is necessary to note, the calculated quantitative data of the phase fraction depending on the alloy annealing temperature are far from experimentally obtained data. However, a qualitative analysis of the change the phase relationship depending on the annealing temperature or chemical composition of the alloy, as well as the chemical composition of the phases is available.

This research project has been sup ported by the Russian Foundation for Basic Research (RFBR) grant for the implementation of the research project № 16-33-01108 (мол_а).

keywords Titanium aluminides, γ-alloys, thermodynamic calculations, solidification, microstructure, phase composition, annealing
References

1. Appel F., Paul J. D. H., Oehring M. Gamma Titanium Aluminide Alloys. Wiley, VCH, 2011. 746 p.
2. Wu X. Review of alloy and process development of TiAl alloys. Intermetallics. 2006. No. 14. pp. 1114–1122.
3. Chladil H. F., Clemens H., Leitner H., Bartels A., Gerling R., Schimansky F. P., Kremmer S., Phase transformations in high niobium and carbon containing gamma-TiAl based alloys. Intermetallics. 2006. No. 14. pp. 1194–1198.
4. Hu D., Wu X., Loretto M. H. Advances in optimization of mechanical properties in cast TiAl alloys. Intermetallics. 2005. No. 13. pp. 914–919.
5. Sung S-Y., Kim Y-J. Modeling of titanium aluminides turbo-charger casting. Intermetallics. 2007. No. 15. pp. 468–474.
6. Liu K., Ma Y., Gao M., Rao G. B., Li Y. Y., Ke W. Single step centrifugal casting TiAl automotive valves. Intermetallics. 2005. No. 13. pp. 925–928.
7. Barbosa J. Silva R. C., Caetano M. A. Influence of superheating on casting of TiAl. Intermetallics. 2007. No. 15. pp. 945–955.
8. Kuang J. P., Harding R. A., Campbell J. Microstructure and properties of investment castings of titanium aluminide. Materials Science and Engineering A. 2002. No. 31. pp. 329–331.
9. Simpkins R. J., Rourke M. P., Bieler T. A., McQuayb P. A. The effect of HIP pore closure and age hardening on primary creep and tensile property variations in a TiAl XD alloy with 0.1 wt.% carbon. Materials Science and Engineering A. 2007. Vol. 463. pp. 208 –215.
10. Harding R. A., Wickins M., Wang H., Djambazov G., Pericleous K. Development of a turbulence-free casting technique for titanium aluminides. Intermetallics. 2011. No. 19. pp. 805–813.
11. Beddoes J., Seo D. Y., Chen W. R., Zhao L. Relationship between tensile and primary creep properties of near-TiAl intermetallics. Intermetallics. 2011. No. 9. pp. 915–922.
12. Hodge A. M., Hsiung L. M., Nieh T. G. Creep of nearly lamellar TiAl alloy containing W. Scripta Materialia. 2004. No. 51. pp. 411–415.
13. Güther V., Rothe C., Winter S., Clemens H. Metallurgy, microstructure and properties of intermetallic TiAl ingots. BHM. Berg and Hüttenmännische Monatshefte. 2010. No. 155. pp. 325–329.
14. Clemens H., Wallgram W., Kremmer S., Güther V., Otto A., Bartels A. Design of novel β-solidifying TiAl alloys with adjustable β/B2-phase fraction and excellent hot-workability. Advanced Engineering Materials. 2008. No. 10. pp. 707–713.
15. Clemens H., Mayer S. Design, processing, microstructure, properties, and applications of advanced intermetallic TiAl alloys. Advanced Engineering Materials. 2013. No. 15. pp. 191–215.
16. Clemens H., Chladil H. F., Wallgram W., Zickler G. A., Gerling R., Liss K. D., Kremmer S., Güther V., Smarsly W. In and ex situ investigations of the -phase in a Nb and Mo containing -TiAl based alloy. Intermetallics. 2008. No. 16. pp. 827–833.
17. Wallgram W., Schmoelzer T., Cha L., Das G., Güther V., Clemens H. Technology and mechanical properties of advanced γ-TiAl based alloys. International Journal of Material Resources. 2009. No. 100. pp. 1021–1030.
18. Kremmer S., Chladil H., Clemens H., Otto A., Güther V. Near conventional forging of titanium aluminides. In: Niinomi M, Akiyama S, Ikeda M, Hagiwari M, Maruyama K, editors. Ti-2007 science and technology. Sendai, Japan: The Japan Institute of Metals (JIM). 2008. pp. 989–992.
19. Kartavykh A.V., Asnis E. A., Piskun N. V., Statkevich I. I., Gorshenkov M. V., Korotitskiy A. V. A promising microstructure/deformability adjustment of β-stabilized γ-TiAl intermetallics. Materials Letters. 2016. Vol. 162. pp. 180–184.
20. Huang Z. W., Voice W., Bowen P. Thermal exposure induced α2 + γ → B2(ω) and α2 → B2(ω) phase transformations in a high Nb fully lamellar TiAl Alloy. Scripta Materialia. 2003. Vol. 48. pp. 79–84
21. Jin Y., Wang J. N., Yang J., Wang Y. Microstructure refinement of cast TiAl alloys by solidification. Scripta Materialia. 2004. No. 51. pp. 113–117.
22. Hao Y. L., Yang R., Cui Y. Y., Li D. The influence of alloying on the α2/(α2 + γ) phase boundaries in TiAl based systems. Acta Materialia. 2000. Vol. 48. pp. 1313–1324.
23. Kainuma R., Fujita Y., Mitsui H., Ishida K. Phase equilibria among α (hcp), β (bcc) and γ (L10) phases in Ti – Al base ternary alloys. Intermetallics. 2000. No. 8. pp. 855–867.
24. Witusiewicz V. T., Bondar A. A., Hecht U., Velikanova T. Ya. The Al–B–Nb–Ti system: IV. Experimental study and thermodynamic reevaluation of the binary Al–Nb and ternary Al – Nb – Ti systems. Journal of Alloys and Compounds. 2009. No. 472. pp. 133–161.
25. Andersson J. O., Helander T., Hoglund L., Shi P. F., Sundman B. Thermo-Calc and DICTRA, computational tools for materials science, Calphad. 2002. Vol. 26. pp. 273–312.
26. Werner R., Schloffer M., Schwaighofer E., Clemens H., Mayer S. Thermodynamic calculations of phase equilibria and phase fractions of a -solidifying TiAl alloy using the CALPHAD approach. MRS Proceedings. 2013. pp. 15–16.
27. Clemens H., Mayer S. Design, processing, microstructure, properties, and applications of advanced intermetallic TiAl alloys. Advanced Engineering Materials. 2013. No. 15. pp. 191–215.
28. Belov N. A., Akopyan T. K., Belov V. D., Gorshenkov M. V., Gershman J. S. The effect of Cr and Zr on the structure and phase composition of TNM gamma titanium aluminide
alloy. Intermetallics. 2017. Vol. 84. pp. 121–129.

Full content Analysis of the phase composition and microstructure of a TNM-type alloy by using thermodynamic calculation
Back