Название Investigation of the additional alloying effect on oxidation during heating of the alloys of aluminum with magnesium
Автор Drits A. M., Rokhlin L. L., Dobatkina T. V., Nikitina N. I., Tarytina I. E.
Информация об авторе A. M. Drits, Director of Technologies, Alcoa SMZ, ZAO «Alkoa SMZ»; L. L. Rokhlin, Chief Researcher, e-mail: rokhlin@ultra.imet.ac.ru; T. V. Dobatkina, Leading Researcher; N. I. Nikitina, Senior Researcher; I. E. Tarytina, Researcher, The Baykov Institute of Metallurgy and Material Science, Russian Academy of Sciences.
Реферат

Effect of calcium and several rare earth metals (Ce, Nd, Sm, Y, Gd, Dy) on oxidation resistance during heating of the aluminum alloys containing 5–6% of Mg was researched. The method where oxidation value was determined by the weight increase after melting was chosen for estimation of the oxidation rate. Investigation indicated that all oxidation to consist on the oxide film formation. At significant oxidation the oxide film thickness on the alloy surfaces equaled 130–170 μm. On the other hand, in samples subjected to weak oxidation the oxide film thickness equaled 20–80 μm. It was shown, that all metals used as additional alloying elements decreased oxidation of the Al–Mg-alloys in molten state. The most oxidation resistance among them was observed in the Al–Mg-alloys containing calcium.
Ключевые слова Aluminum alloys, additional alloying, calcium, rare earth metals, oxidation, oxidation film.
Библиографический список

1. Konstruktsionnye materialy : spravochnik (Construction materials: reference book). Ed. B. N. Arzamasova. Moscow, 1990. pp. 234-272.

2. Mashinostroenie : entsiklopediya ; v 40 t. (Machine-building industry: encyclopedia. In 40 books). Ed. I. N. Fridlyandera, E. T. Dolbenko. Moscow, 2001. Part. II-3. p. 26.

3. International Alloy Designations and Chemical Composition Limits for Wrought Aluminum and Wrought Aluminum Alloys. Registration Record Series. Arlington (VA) : Aluminum Association, Inc., 2006. pp. 1-28.

4. Emli E. F. Osnovy tekhnologii proizvodstva i obrabotki magnievykh splavov (Basis of technology of magnesium alloys production and treatment). Moscow, 1972.

5. Drits M. E. Magnievye splavy dlya raboty pri povyshennykh temperaturakh (Magnesium alloys for operations under the conditions of high temperature). Moscow, 1964.

6. Rokhlin L. L. Magnievye splavy, soderzhashchie redkozemelnye metally (Magnesium alloys, contained rare-earth metals). Moscow, 1980.

7. Diagrammy sostoyaniya dvoynykh metallicheskikh sistem : spravochnik (Phasing diagrams of double metal systems: reference book). Ed. N. P. Lyakisheva. Moscow, 1996. Part. 1. pp. 167-170.

8. Drits M. E., Bochvar N. R., Kadaner E. S. et al. Diagrammy sostoyaniya sistem na osnove alyuminiya i magniya : spravochnik (Phasing diagrams of systems on the base of aluminium and magnesium: reference book). Moscow, 1977. pp. 71-72.
Language of full-text русский
Полный текст статьи Получить
Назад