60th anniversary of Dept. of Materials Technology of Volgograd State Technical University
Название Causes of low casting ability for continuously cast billets from 08Kh18N10T steel and development of measures directed on increase of casting sequence
DOI 10.17580/chm.2024.05.04
Автор D. V. Rutskiy, A. N. Bozheskov, N. A. Zyuban, A. A. Shuklin
Информация об авторе

Volgograd State Technical University, Volgograd, Russia
D. V. Rutskiy, Cand. Eng., Associate Prof., Head of Dept. of Materials Technology, e-mail: drutskii@vstu.ru
N. A. Zyuban, Dr. Eng., Prof., Dept. of Materials Technology
A. A. Shuklin, Postgraduate Student, Dept. of Materials Technology

JSC “Volzhsky Pipe Plant“, Volzhsky, Russia

A. N. Bozheskov, Chief Engineer, e-mail: vtz@vtz.ru

Реферат

Currently, continuous casting is one of the main ways to obtain ingots for subsequent metallurgical processing in the conditions of modern metallurgical enterprises. At the same time, one of the main problems is the organization and maintenance of high sequence of the process, since one of the main technological parameters affecting the cost of production of continuously cast billets is the casting ability of steel in continuous casters. When mastering the production of continuously cast billets from stainless steel grades on existing steelmaking units, problems arise related to poor casting ability. It was found in this work that the reason for the low casting ability in production of stainless steels is the release of refractory oxide (TiO and Al2O3–TiO2) and oxynitride (Al2O3–TiO2 and TiN) inclusions in deposits on the walls of the steel filling tract. The research used optical and electron microscopy methods with an automatic particle analyzer (EDAX Partical/Phase Analysis Software). Identification of non-metallic inclusions in the samples taken at the stages of ladle treatment and casting showed that oxide inclusions (TiO and Al2O3–TiO2), formed after the introduction of FeTi, before the second stage of vacuum processing, nitride (TiN) and oxynitride inclusions (Al2O3–TiO2 and TiN), are formed during continuous casting and solidification of continuously cast billets. Based on the conducted research, measures are proposed aimed at preventing the formation of refractory non-metallic inclusions containing titanium, which made it possible to increase the sequence of casting on existing steelmaking units in the electric steelmaking shop. The increase in serial production to two melts per series led to a reduction in the consumption of the metal coefficient in the production of continuously cast billets by 20 kg/t, as well as to a reduction in the cost of tundish refractories.

Ключевые слова Ladle treatment, vacuum processing, continuous casting, non-metallic inclusions, calcium aluminates, titanium oxides and nitrides
Библиографический список

1. Agarkov A. Yu., Rutskiy D. V., Zyuban N. A., Babin G. V. et al. Reveal of nature of forming scabs at internal wall of a pouring nozzle during continuous casting of S45E steel. Teoriya i tekhnologiya metallurgicheskogo proizvodstva. 2020. No. 1 (32). pp. 11–17.
2. Lukavaya M. S., Mikhailov G. G. Analysis of sculling process of pouring nozzles during continuous casting of steel. Vestnik YuUrGU. Seriya “Metallurgiya”. 2006. Vol. 7. No. 10. pp. 69–72.
3. Vdovin K. N., Rusakov A. V., Lisichkina K. A. Prevention of sculling of pouring nozzles during casting of steels, which are deoxidized by aluminium. Metallurg. 2008. No. 6. pp. 36–37.
4. Zyuban N. A., Rutskii D. V., Nikitin M. S., Kirilichev M. V. Research and analysis of causes of the steel-pouring tract sculling during S45E steel production. Chernye metally. 2023. No. 10. pp. 70–77.
5. Wasai K., Mukai K., Miyanaga A. Observation of inclusion in aluminum deoxidized iron. ISIJ International. 2002. Vol. 42, Iss. 5. pp. 459–466. DOI: 10.2355/isijinternational.42.459
6. Yang W., Zhang L., Wang X., Ren Y. et al. Characteristics of inclusions in low carbon Al-killed steel during ladle furnace refining and calcium treatment. ISIJ International. 2013. Vol. 53, Iss. 8. pp. 1401–1410. DOI: 10.2355/isijinternational.53.1401
7. Khoroshilov A. D., Somov S. A., Katolikov V. D., Murysev V. A. et al. Experience of use of calciumcontaining injection wire with filling from electrolytic calcium at the stage of ladle furnace steel treatment. Izvestiya vuzov. Chernaya metallurgiya. 2023. Vol. 66. No. 3. pp. 337–343.
8. Golubtsov V. A., Ryabchikov I. V. The ways of lowering of possibility of sculling for steel pouring nozzles during steel casting. Chernaya metallurgiya. Byulleten nauchno-tekhnicheskoy i ekonomicheskoy informatsii. 2011. No. 12. pp. 50–53.
9. Zhou Shi-kai. Study of sculling of a pouring nozzle погружного стакана during continuous casting of stainless steel RE-253MA. Metallurg. 2013. No. 6. pp. 49–53.
10. Bozheskov A. N. Research and improvement of steel ladle treatment technology and continuous casting with rated low limit of aluminium and sulfur content in order to increase its casting ability. Dissertation … of a Candidate of technical sciences. Мoscow. 2019.
11. Patent 2285727, C21C 7/04, RF. The method of steel production with rated sulfur content. Andrianov N. V. et al. Bulletin No. 29. Announced: 10.06.2006; published: 20.10.2006.
12. GOST 1778–70 (ISO 4967–79) Steel. Metallographic methods for determination of nonmetallic inclusions. Introduced: 01.01.1972.
13. Lind M., Holappa L. Transformation of alumina inclusions by calcium treatment. Metallurgical and Materials Transactions B. 2010. Vol. 41. pp. 359–366. DOI: 10.1007/s11663-009-9337-9
14. Pretorius E., Oltmann H., Cash T. The effective modification of spinel inclusions by Ca treatment in LCAK steel. Iron Steel Technol. 2010. Vol. 7. pp. 31–44.
15. Yang S., Wang Q., Zhang L., Li J., Peaslee K. Formation and modification of MgO∙Al2O3-based inclusions in alloy steels. Metall. Mater. Trans. B. 2012. Vol. 43. pp. 731–750.
16. Bakin I. V., Shaburova N. A., Ryabchikov I. V., Mizin V. G. et al. Experimental research of steel refining and modifying be the alloys Si – Ca, Si – Sr and Si – Ba. Stal. 2019. No. 8. pp. 14–18.
17. Agarkov A. Yu., Rutskiy D. V., Zyuban N. A., Babin G. V. Estimation of the influence of melt processing with Ca- and Ba-containing wire on the phase composition and contamination with non-metallic inclusions during ladle furnace treatment and casting of 26KhMFBA steel. Chernye metally. 2021. No. 12. pp. 36–44.
18. Yi Wang, Chang-rong Li, Lin-zhu Wang, Xing-qiang Xiong et al. Effect of yttrium treatment on alumina inclusions in high carbon steel. J. Iron Steel Res. Int. 2022. Vol. 29. pp. 655–664. DOI: 10.1007/s42243-021-00633-y
19. Belov B. F., Ryabchikov I. V., Bakin I. V., Mizin V. G. et al. Steel deoxidizing by binary and multicomponent alloys of rare-earth metals. Stal. 2020. No. 7. pp. 14–18.

Language of full-text русский
Полный текст статьи Получить
Назад