Журналы →  Tsvetnye Metally →  2022 →  №9 →  Назад

SCIENTIFIC DEVELOPMENTS OF THE D. MENDELEEV UNIVERSITY OF CHEMICAL TECHNOLOGY OF RUSSIA
Название Black protective molybdate coatings obtained on galvanized steel
DOI 10.17580/tsm.2022.09.03
Автор Abrashov A. A., Grigoryan N. S., Aleshina V. Kh., Shloma O. A.
Информация об авторе

D. Mendeleev University of Chemical Technology of Russia, Moscow, Russia:

A. A. Abrashov, Associate Professor at the Department of Innovative Materials and Corrosion Protection, Candidate of Technical Sciences, e-mail: abrashov.a.a@muctr.ru
N. S. Grigoryan, Professor at the Department of Innovative Materials and Corrosion Protection, Associate Professor, Candidate of Chemical Sciences, e-mail: grigorian.n.s@muctr.ru
V. Kh. Aleshina, Assistant Lecturer at the Department of Innovative Materials and Corrosion Protection, e-mail: aleshinavh@gmail.com
O. A. Shloma, Undergraduate Student at the Department of Innovative Materials and Corrosion Protection, e-mail: okshloma@yandex.ru

Реферат

This paper looks at the passivation of zinc in environmentally safe molybdate solutions with the aim to replace highly toxic solutions used in black chromate passivation. It is shown that higher current density and process duration make black coatings more saturated. However, this affects the adhesion of the deposited layers. The optimum pH of the solution was found to be in the range from 4.0 to 4.3 units. At the same time, poor quality coatings are obtained outside the above range. It was also found that the process duration can be reduced from 3–6 to 2–5 min by lowering the pH of the solution from 5 to 4 units. The colour of the coatings changes from the colour of the rainbow to black depending on the process duration, current density and the temperature of the working solution. The coatings of deep black colour are formed at the process time of 2 to 5 min, current density of 0.7 to 0.8 A/dm2 and temperature of 50 to 65 oC. Spectral studies showed that molybdate coatings that were produced in optimal conditions consist of molybdenum(VI) oxide, molybdenum(IV) oxide, molybdenum(IV) oxide-hydroxide, zinc oxide, as well as zinc and nickel hydroxides. It should be noted that molybdenum is predominantly integrated in the coating in the form of MoO2. The authors have developed an electrochemical process for the deposition of protective black molybdate coatings on galvanized surfaces in the following solution, g/L: 15–19 (NH4)6Mo7O24; 16 CH3COONa; 4 NiSO4·6H2O. This process helps obtain compact coatings corresponding to 10 on a ten-point black colour scale in the following conditions: i = 0.7–0.8 A/dm2, t = 50–65 оC, = 7–10 min and pH = 4.0–4.3.
The authors would like to thank the Mendeleev Shared Knowledge Centre for support of this research.

Ключевые слова Corrosion protection, surface treatment, passivation of galvanized steel, molybdate coatings, chromate-free passivation, black decorative coatings, black light absorbing coatings
Библиографический список

1. Dingwerth B. Black chromium plating of zinc and its alloys followed by finishing in a trivalent chromium passivation solution. Galvanotekhnika i obrabotka poverkhnosti. 2009. Vol. 17, No. 1. pp. 38–48.
2. Long Z. L., Zhou Y. C., Xiao L. Characterization of black chromate conversion coating on the electrodeposited zinc – iron alloy. Applied Surface Science. 2003. Vol. 218, No. 1-4. pp. 124–137.
3. Pintuperakovit N., Mohammed W., Visuttipitukul P., Sukkasi S. et al. The influence of current density for zinc electrodeposition on color appearance of black trivalent chromate conversion coatings. Key Engineering Materials. 2015. Vol. 658. pp. 161–166.
4. Gigandet M. P., Faucheu J., Tachez M. Formation of black chromate conversion coatings on pure and zinc alloy electrolytic deposits: role of the main constituents. Surface and Coatings Technology. 1997. Vol. 89, No 3. pp. 285–291.
5. Directive 2011/65/EU (RoHS II) of the European Parliament and of the Council of 8 June 2011 on the restriction of the use of certain hazardous substances in electrical and electronic equipment.
6. Directive 2002/96/EC of the European Parliament and of the Council of 27 January 2003 on waste electrical and electronic equipment.
7. Directive 2000/53/EC of the European Parliament and of the Council of 18 September 2000 on end-of life vehicles. Official Journal of the European Communities L269. pp. 34–43.
8. Regulation (EC) No 1907/2006 of the European Parliament and 2357 of the Council of 18 December 2006 concerning the Registration, Evaluation, Authorisation and Restriction of Chemicals (REACH) and establishing a European Chemicals Agency.
9. Kuzin E. N., Chernyshev P. I., Vizen N. S., Krutchinina N. E. The purification of the galvanic industry wastewater of chromium(VI) compounds using titanium(III) chloride. Russian Journal of General Chemistry. 2018. Vol. 88, No. 13. pp. 2954–2957.
10. Kuzin E. N., Kruchinina N. E., Nosova T. I. Electroplating wastewater treatment. Tsvetnye Metally. 2021. No. 10. pp. 50–54. DOI: 10.17580/tsm. 2021.10.07.
11. Fachikov L., Ivanova D. Surface treatment of zinc coating by molybdate solutions. Applied Surface Science. 2012. Vol. 258. pp. 10160–10167.
12. Wharton J. A., Ross D. H., Treacy G. M. et al. An EXAFS investigation of molybdate-based conversion coatings. Journal of Applied Electrochemistry. 2003. Vol. 33. pp. 553–561.
13. Konno H., Narumi K., Habazaki H. Molybdate/Al(III) composite films on steel and zinc-plated steel by chemical conversion. Corrosion Science. 2002. Vol. 44. pp. 1889–1900.
14. Magalhaes A. A. O., Margarit I. C. P., Mattos O. R. Molybdate conversion coatings on zinc surfaces. Journal of Electroanalytical Chemistry. 2004. Vol. 572. pp. 433–440.

15. Song Y. K., Mansfeld F. Development of a molybdate – phosphate – silane – silicate (MPSS) coating process for electrogalvanized steel. Corrosion Science. 2006. Vol. 48. pp. 54–164.
16. Meshalkin V. P., Abrashov A. A., Vagramyan T. A., Grigoryan N. S. et al. Development of composition and investigation of properties of a new, environmentally friendly molybdenum-containing decorative protective conversion coating on zinс-plated surfaces. Doklady Chemistry. 2018. Vol. 480, No. 5. pp. 555–558.
17. Woicik J. C. Hard X-ray photoelectron spectroscopy (HAXPES). Switzerland Springer International Publishing : ChamCity, 2016. 571 p.
18. Shirley D. A. High-resolution X-ray photoemission spectrum of the valence bands of gold. Physical Review. 1972. Vol. 5. pp. 4709–4713.
19. Scofield H., Hartree-Slater J. Subshell photoionization cross-sections at 1254 and 1487 eV. Journal of Electron Spectroscopy and Related Phenomena. 1976. Vol. 8. pp. 129–137.
20. Mohai M. XPS MultiQuant: multimodel XPS quantification software. Surface and Interface Analysis. 2004. Vol. 36. pp. 828–832.
21. Cumpson P. J., Seah M. P. Elastic scattering corrections in AES and XPS. II. Estimating attenuation lengths and conditions required for their valid use in Overlayer, Substrate experiments. Surface and Interface Analysis. 1997. Vol. 25. pp. 430–446.
22. Grigoryan N. S., Abrashov A. A., Vagramyan T. A., Kostyuk A. G. Passivation of ferrous and non-ferrous metals in the solution containing gallic acid esters. Chemistry and Technology of Organic Substances. 2017. No. 4. pp. 55–63.
23. Aleshina V. Kh., Abrashov A. A., Grigoryan N. S., Vagramyan T. A. Passivation of zinc coatings in molybdate solutions. Tsvetnye Metally. 2021. No. 10. pp. 20–25. DOI: 10.17580/tsm.2021.10.02.

Language of full-text русский
Полный текст статьи Получить
Назад