ArticleName Structural features of hydrogenated E110opt and E635 tubes
DOI 10.17580/nfm.2023.01.07
ArticleAuthor Isaenkova M. G., Petrov M. I., Kozlov I. V., Bogomolova A. V.
ArticleAuthorData

National Research Nuclear University “MEPhI”:

M. G. Isaenkova, Professor, Doctor of Physical and Mathematical Sciences, e-mail: MGIsaenkova@mephi.ru
M. I. Petrov, Engineer, e-mail: mipetrov.99@yandex.ru
I. V. Kozlov, Engineer, e-mail: ilya_mephist@mail.ru
A. V. Bogomolova, Engineer, e-mail: bogomolova@m-a-l.ru

Abstract

The paper investigates the behavior of the hydride phase in hydrogenated tubes made of Russian zirconium E635 and E110opt alloys. The orientation and fraction of mesoscale hydrides in the alloy matrix have been described by analyzing optical metallographic images using the developed software. Metallographic images were used to assess the predominant orientation of hydrides in the axial section of the tube, as well as the surface density of the hydride phase with an increase in the concentration of hydrogen in tubes made of different alloys. It has been shown that increasing the hydrogen concentration to 600–700 wppm increases the number of radially oriented hydrides, which is associated with the development of compressive radial stress during the formation of tangentially oriented hydrides at the initial stage. Increasing the hydrogen concentration in E110opt alloy cladding tubes to 600–700 wppm leads to a change in the orientation of the α-zirconium basal axes, which results in an increase in the integral textural fR-parameter and a decrease in the fT- and fL-parameters. This change is due to the development of radial compressive stress and is only possible due to the activation of twinning in the grains, the basal axes of which are deflected from the compressive stress at an angle of up to 90 degrees. The results of synchrotron Debye rings and X-ray reflection diffraction analysis revealed patterns of structure and texture formation of zirconium matrix and hydrides with increasing hydrogen concentration in E110opt and E635 tube materials. Twinning by the {1012}<1011> and {1011}<1012> systems has been detected in the alloy E110opt. It reorients the basal axes at angles of 85o and 57.2o in the direction of compressive stress applied in the radial direction. According to the crystal lattice geometry of the α-phase, this reorientation occurs in the direction deviated from the radial direction by 30 degrees. It has been established that in E635 alloy hydrides with {001}<110> orientation are predominantly formed, but hydrides with additional {110}<011> and {110}<112> orientations are also present in smaller amounts. In the E110opt alloy there are hydrides of {001}<110> and {110}<011> orientations as well as <112> in approximately equal proportions. The presence of hydrides with a <112> partially axial textural component is due to activation in the α-phase of twinning along the {1012} and {1011} planes, in which hydrides are formed according to the established orientation relationship (0001)α – Zr || {111}α – ZrH1.66.

The work was carried out with the financial support of the Russian Federation represented by the Ministry of Science and Higher Education of the Russian Federation (Agreement No. 075-15-2021-1352).
The authors are grateful for the provision of samples for research to the Joint-Stock Company “Advanced Research Institute of Inorganic Materials named after Academician A. A. Bochvar” and his employees Plyasov A. A. and Saburov N. S., as well as the employees of the National Research Nuclear University MEPhI Fesenko V. A. and Mikhalev N. A.

keywords Zirconium alloys, hydrides orientation, microstructure, crystallographic texture, X-ray, synchrotron radiation, orientation relationship
References

1. Zaimovsky A. S., Nikulina A.V., Reshetnikov N. G. Zirconium Alloys in Nuclear Power Engineering. 2nd ed., rev. and suppl. Moscow: Energoatomizdat, 1994. 252 p.
2. Douglass D. L. The Metallurgy of Zirconium. Transl. from Eng. Moscow: Atomizdat, 1975. 360 p.
3. Lemaignan C., Motta A. T. Zirconium Alloys in Nuclear Applications. In: Materials Science and Technology. Weinheim, Germany: Wiley-VCH Verlag GmbH & Co. KGaA, 2006.
4. Lee J. M., Hong S. I. Design and Mechanical Characterization of a Zr – Nb – O – P Alloy. Materials and Design. 2011. Vol. 32, Iss. 8-9. pp. 4270–4277.
5. Delayed Hydride Cracking in Zirconium Alloys in Pressure Tube Nuclear Reactors: Final Report of a Coordinated
Research Project 1998–2002. Vienna: International Atomic Energy Agency, 2004. 85 p.
6. Delayed Hydride Cracking of Zirconium Alloy Fuel Cladding: IA EA Tecdoc Series No. 1649. Vienna: IAEA, 2010. 66 p.
7. Tan J., Ying S., Li C., Sun C. Effect of Zirconium Hydrides on Cyclic Deformation Behavior of Zr – Sn – Nb Alloy. Scripta Materialia. 2006. Vol. 55, Iss. 6. pp. 513–516.
8. Lee K. W., Hong S. I. Zirconium Hydrides and Their Effect on the Circumferential Mechanical Properties of Zr –
Sn – Fe – Nb Tubes. Journal of Alloys and Compounds. 2002. Vol. 346, Iss. 1. pp. 302–307.
9. Puls M. P. The Effect of Hydrogen and Hydrides on the Integrity of Zirconium Alloy Components. Delayed Hydride Cracking. London: Springer-Verlag, 2012. 475 p.

10. Motta A. T., Capolungo L., Chen L.-Q., Cinbiz M. N., Daymond M. R., Koss D. A., Lacroix E., Pastore G., Simon P.-C. A., Tonks M. R., Wirth B. D., Zikry M. A. Hydrogen in Zirconium Alloys: a Review. Journal of Nuclear Materials. 2019. Vol. 518. pp. 440–460.
11. B. Cox, C. Roy. The Use of Tritium as a Tracer in Studies of Hydrogen Uptake by Zirconium Alloys, vol. 2519, Atomic Energy of Canada Ltd., Chalk River Nuclear Laboratories AECL, 1965.
12. Chu H. C., Wu S. K., Kuo R. C. Hydride Reorientation in Zircaloy-4 Cladding. Journal of Nuclear Materials. 2008. Vol. 373, Iss. 1-3. pp. 319–327.
13. De Menibus A. H., Auzoux Q., Dieye Q., Berger P., Bosonnet S., Foy E., Macdonald V., Besson J., Crépin J. Formation and Characterization of Hydride Blisters in Zircaloy-4 Cladding Tubes. Journal of Nuclear Materials. 2014. Vol. 449, Iss. 1-3. pp. 132–147.
14. Jeong Y. H., Kim H. G., Kim T. H. Effect of β Phase, Precipitate and Nb-concentration in Matrix on Corrosion and Oxide Characteristics of Zr-xNb Alloys. Journal of Nuclear Materials. 2003. Vol. 317, Iss. 1. pp. 1–12.
15. Jeong Y. H., Kim H. G., Kim D. J., Choi B. K., Kim J. H. Influence of Nb Concentration in the α-matrix on the Corrosion Behavior of Zr-xNb Binary Alloys. Journal of Nuclear Materials. 2003. Vol. 323, Iss. 1. pp. 72–80.
16. Motta A. T., Couet A., Comstock R. J. Corrosion of Zirconium Alloys Used for Nuclear Fuel Cladding. Annual Review of Materials Research. 2015. Vol. 45, Iss. 1. pp. 311–343.
17. Singh R. N., Kishore R., Sinha T. K, Kashyap B. P. Hydride Blister Formation in Zr-2.5wt%Nb Pressure Tube Alloy. Journal of Nuclear Materials. 2002. Vol. 301, Iss. 2-3. pp. 153–164.
18. Pierron O. N., Koss D. A., Motta A. T., Chan K. S. The Influence of Hydride Blisters on the Fracture of Zircaloy-4. Journal of Nuclear Materials. 2003. Vol. 322, Iss. 1. pp. 21–35.
19. Raynaud P. A., Koss D. A., Motta A. T. Crack Growth in the Through-Thickness Direction of Hydrided Thin-Wall Zircaloy Sheet. Journal of Nuclear Materials. 2012. Vol. 420, Iss. 1-3. pp. 69–82.
20. Perryman E. C. W. Pickering Pressure Tube Cracking Experience. Nuclear Energy. 1978. Vol. 17, Iss. 2. pp. 95–105.
21. Platonov P. A., Ryazantseva A. V., Saenko G. P. et al. The Study of the Cause of Cracking in Zirconium Alloy Fuel Channel Tubes: Poster Paper. In: ASTM Zirconium in the Nuclear Industry – 8th International Symposium (available as AECL report RC-87, 1988).
22. Obukhov A.V. Reactor’s Irradiation Effect and Post-Radiation Annealing on the Elemental Composition And Crystal Structure Of The Second Phases In Zirconium Alloys E110 and E635. A Dissertation … Candidate of Technical Sciences. Ulyanovsk, 2022. 143 p.
23. Shishov V. N. Regularities and Mechanisms of Formation of the Microstructure of Zr – Nb – (Fe – Sn – O) Alloys and its Evolution Under Neutron Irradiation. An Abstract … Doctor of Technical Sciences. Moscow, 2012. 47 p.
24. Kearns J. J., Woods C. R. Effect of Texture, Grain Size, and Cold Work on the Precipitation of Oriented Hydrides in Zircaloy Tubing and Plate. Journal of Nuclear Materials. 1966. Vol. 20, Iss. 3. pp. 241–261.
25. Markelov V. A. Improving the Composition and Structure of Zirconium Alloys to Ensure the Operability of Fuel Rods (TVEL), Fuel Assemblies (TVS) and Pressure Pipes of the Active Zones of Water-Cooled Reactors with Increased Resource and Fuel Burnout. An Abstract … Doctor of Technical Sciences. Moscow, 2010. 46 p.
26. Coleman C. E. Effect of Texture on Hydride Reorientation and Delayed Hydrogen Cracking in Cold-Worked Zr-2.5Nb. Zirconium in the Nuclear Industry: 5th Conference. 1982, pp. 393–411.
27. Kiran Kumar N. A. P., Szpunar J. A., He Z. Preferential Precipitation of Hydrides in Textured Zircaloy-4 Sheets. Journal of Nuclear Materials. 2010. Vol. 403, Iss. 1-3. pp. 101–107.
28. Roy C., Jacques J. G. {1017} Hydride Habit Planes in Single Crystal Zirconium. Journal of Nuclear Materials. 1969. Vol. 31, Iss. 2. pp. 233–237.
29. Arunachalam V. S., Lentinen B., Östberg G. The Orientation of Zirconium Hydride on Grain Boundaries in Zircaloy-2. Journal of Nuclear Materials. 1967. Vol. 21. pp. 241–248.
30. Ambler G. F. R. Grain boundary hydride habit in Zircaloy-2. Journal of Nuclear Materials. 1968. Vol. 28, Iss. 3. pp. 237–245.
31. Perovic V., Weatherly G. C., Simpson C. J. Hydride Precipitation in α/β Zirconium Alloys. In: Perspectives in Hydrogen in Metals: Collected Papers on the Effect of Hydrogen on the Properties of Metals and Alloys. 1986. pp. 469–479.
32. Perovic V., Weatherly G. C. The Nucleation of Hydrides in a Zr-2.5 wt% Nb Alloy. Journal of Nuclear Materials. 1984. Vol. 126. pp. 160–169.
33. Perovic V., Weatherly G. C., MacEwen S. R., Leger M. The influence of Prior Deformation on Hydride Precipitation in Zircaloy. Acta Metallurgica et Materialia. 1992. Vol. 40, Iss. 2. pp. 63–372.
34. Yu. Udagawa, Yamaguchi M., Abe H., Sekimura N., Fuketa T. Ab Initio Study on Plane Defects in Zirconium– Hydrogen Solid Solution and Zirconium Hydride. Acta Materialia. 2010. Vol. 58, Iss. 11. pp. 3927–3938.
35. Bai J. B., Prioul C., Francois D. Hydride Embrittlement in Zircaloy-4 Plate: Part I. Influence of Microstructure on the Hydride Embrittlement in Zircaloy-4 at 20 °C and 350 °C. Metallurgical and Materials Transactions: A. 1994. Vol. 25, Iss. 6. pp. 1185–1197.
36. Bai J.B., JI N., Gilbon D., Prioul C., François D. Hydride Embrittlement in Zircaloy-4 Plate: Part II. Interaction Between the Tensile Stress and the Hydride Morphology. Metallurgical and Materials Transactions. 1994. Vol. 25A. pp. 1199–1208.
37. Wang Z., Garbe U., Li H., Wang Y., Studer A. J., Sun G., Harrison R. P., Liao X., Vicente Alvarez M. A., Santisteban J. R., Kong C. Microstructure and Texture Analysis of δ-hydride Precipitation in Zircaloy-4 Materials by Electron Microscopy and Neutron Diffraction. Journal of Applied Crystallography. 2014. Vol. 47, Iss. 1. pp. 303–315.
38. Kim Y. S., Perlovich Yu., Isaenkova M., Kim S. S., Cheong Y. M. Precipitation of Кeoriented Hydrides and Textural Change of α-Zirconium Grains During Delayed Hydride Cracking of Zr – 2.5% Nb Pressure Tube. Journal of Nuclear Materials. 2001. Vol. 297. pp. 292–302.

39. Kim J. S., Kim S. D., Yoon J. Hydride Formation on Deformation Twin in Zirconium Alloy. Journal of Nuclear Materials. 2016. Vol. 482. pp. 88–92.
40. Kiran Kumar N. A. P., Szpunar J. A. EBSD Studies on Microstructure and Crystallographic Orientation of δ-hydrides in Zircaloy-4, Zr – 1% Nb and Zr – 2.5% Nb. Materials Science and Engineering: A. 2011. Vol. 528, Iss. 21. pp. 6366–6374.
41. Tenishev A.V. Differential Scanning Calorimetry Determination of the Hydrogen Solubility in E110opt and E635 Zirconium Alloys. Russian Metallurgy. 2022. № 6. pp. 1427–1433.
42. Perlovich Yu., Isaenkova M., Fesenko V. Use of Gene ralized Pole Figures in the X-ray Study of Textured Metal Materials. Zietschrift fur Kristallographie. 2007. Iss. 26. pp. 327–332.
43. Perlovich Yu. A., Isaenkova M. G., Krymskaya O. A., Fesenko V. A., Babich Y. A. Optimization of the Procedure for Determining Integral Texture Parameters of Products from Zirconium-Based Alloys Using the Orientation Distribution Function. IOP Conference Series: Materials Science and Engineering. 2016. Vol. 130. 012056.
44. MTEX Software for Analyzing and Modeling Crys tal lographic Textures by Means of EBSD or Pole Figure Data. TU Chemnitz, Germany. URL: http://mtex-toolbox.github.io/Documentation (Accessed: 05.06.2023).
45. LaboTex v. 3.0 by LaboSoft – Krakow, Poland. URL: http://www.labosoft.com.pl (Accessed: 22.05.2023).
46. Lutterotti L., Vasin R., Wenk H.-R. Rie tveld Texture Analysis from Synchrotron Diffraction Images. I. Calibration and Basic Analysis. Powder Diffraction. 2014. Vol. 29, Iss. 1. pp. 76–84.
47. Wenk H.-R., Lutterotti L., Kaercher P., Kanitpanyacharoen W., Miyagi L., Vasin R. Rietveld Texture Analysis from Synchrotron Diffraction Images. II. Complex Multiphase Materials and Diamond Anvil Cell Experiments. Powder Diffraction. 2014. Vol. 29, Iss. 3. pp. 220–232.
48. Isaenkova M. G., Perlovich Yu. A. Regularity of the Вevelopment of Crystallographic Texture and Substructural Heterogeneity in Zirconium Alloys During Deformation and Heat Treatment. Moscow: “MEPhI”, 2014. 528 p.
49. Isaenkova M. G., Perlovich Y. A., Fesenko V. A., Krymskaya O. A., Krapivka N. A., Tkhu S. S. Regularities of Recrystallization of Rolled Single Crystals And Polycrystals of Zirconium and Alloy Zr – 1%Nb. Physics of Metals and Metallography. 2014. Vol. 115, Iss. 8. pp. 807–815.

Full content Structural features of hydrogenated E110opt and E635 tubes
Back