Journals →  Tsvetnye Metally →  2018 →  #8 →  Back

METAL PROCESSING
ArticleName Processing of aluminum melts using screen filters impregnated with slurry of salt quench baths
DOI 10.17580/tsm.2018.08.12
ArticleAuthor Grachev A. N., Leushin I. O., Deev V. B., Koshelev O. S.
ArticleAuthorData

FGBOU VO “Nizhny Novgorod State Technical University named after R. E. Alekseev”, Nizhny Novgorod, Russia:
A. N. Grachev, Associate Professor of the Department of Metallurgical Technologies and Equipment
I. O. Leushin, Head of Department of Metallurgical Technologies and Equipment
O. S. Koshelev, Professor of Chair of Machine-Building Technological Complexes

 

NUST MISiS, Moscow, Russia:

V. B. Deev, Professor of Department of Foundry Technologies and Art Processing of Materials

Abstract

The analysis of characteristics and properties of thermal production waste in the form of slurry of salt quenching baths is carried out. The preconditions for the use of slurry as a material for the production of active mesh filters with regard to aluminum melts are noted: 1) compliance with the degree of exposure to the human body of the 3rd hazard class in accordance with GOST 12.1.007–76 (substances with moderately hazardous substances); 2) the total content of up to 30% NaCl, KCl, MgCl2; 3) content of up to 36% of BaCO3; 4) the possibility of hardening the water-diluted slurry in the course of thermal drying without the use of binding materials; 5) low cost in comparison with the materials traditionally used for silumin treatment (fluorides, chlorides, carbonates), because sludge is a waste of production, and the costs arising from its use are caused by the need for preparatory operations. The preparation of slurry of salt quenching baths for obtaining an active glass mesh impregnation with respect to aluminum melts, as well as the process of making mesh filters are described. The results of a comparative evaluation of the mechanical properties of cast and thermally processed samples from an aluminum alloy AK5M2 using the obtained screen filters and without them, as well as the results of metallographic analysis are presented. The evaluation showed the effectiveness of the obtained filters in relation to: purification of the melt from nonmetallic inclusions; decrease of the porosity score from the 3rd to the 1st according to GOST 1583–93; increase in hardness of thermally untreated samples by 2.7–24.2%; decrease in hardness of thermally processed samples by 13.2–19.5%; increase in the temporary resistance to breaking of thermally processed samples by 8.3–9.3%; reduction of the time resistance to tearing the specimen without thermal treatment by 1.5%; increase in the time resistance to tearing the sample after heat treatment by 3.4–4.5%; reduction in the size of the α-Al dendrite on average from 35 to 24 μm; reduction in the size of the triple eutectic (Al + Si + β-FeSiAl5) from 56 to 47 μm.

keywords Industrial waste, slurry of salt quenching bath, sodium chloride, potassium chloride, barium carbonate, foundry industry, filtration refining, screen filters, fluxes, nonmetallic inclusions, aluminum alloys, mechanical properties, microstructure
References

1. Prusov E. S., Panfilov A. A. Properties of cast aluminum-based composite alloys reinforced by endogenous and exogenous phases. Russ. Metall. 2011. No. 7. pp. 670–674.
2. Prusov E. S., Panfilov A. A. Influence of repeated remeltings on formation of structure of castings from aluminium matrix composite alloys. Metal 2013: Proc. 22-nd Int. conf. on metallurgy and materials. 2013. No. 1. pp. 1152–1156.
3. Nikitin K. V., Nikitin V. I., Timoshkin I. Yu., Glushchenkov V. A., Chernikov D. G. Melt treatment by pulsed magnetic fields aimed at controlling the structure and properties of industrial silumins. Russian journal of non-ferrous metals. 2016. Vol. 57, Iss. 3. pp. 202–210.
4. Timoshkin I. Y., Nikitin K. V., Nikitin V. I., Deev V. B. Influence of treatment of melts by electromagnetic acoustic fields on the structure and properties of alloys of the Al–Si system. Russian Journal of Non-Ferrous Metals. 2016. Vol. 57. Iss. 5. pp. 419–423.
5. Ivanov Y. F., Alsaraeva K. V., Gromov V. E., Popova N. A., Konovalov S. V. Fatigue life of silumin treated with a high-intensity pulsed electron beam. Journal of Surface Investigation X-ray, Synchrotron and Neutron Techniques. 2015. Vol. 9, Iss. 5. pp. 1056–1059.
6. Ivanov Y. F., Alsaraeva K. V., Gromov V. E., Konovalov S. V., Semina O. A. Evolution of Al – 19,4 Si alloy surface structure after electron beam treatment and high cycle fatigue. Mater. Sci. Technol. (UK). 2015. Vol. 31, Iss. 13a. pp. 1523–1529.
7. Deev V. B., Ponomareva K. V., Prikhodko O. G., Smetanyuk S. V. Influence of temperatures of melt overheating and pouring on the quality of aluminum alloy lost foam castings. Russian Journal of Non-Ferrous Metals. 2017. Vol. 58. Iss. 4. pp. 373–377.
8. Deev V. B., Ponomareva K. V., Yudin A. S. Investigation into the density of polystyrene foam models when implementing the resource-saving fabrication technology of thin-wall aluminum sheet. Russian Journal of Non-Ferrous Metals. 2015. Vol. 56. Iss. 3. pp. 283–286.
9. Deev V. B., Degtyar V. A., Kutsenko A. I., Selyanin I. F., Voitkov A. P. Resource-saving technology for the production of cast aluminum alloys. Steel in Translation. 2007. Vol. 37. Iss. 12. pp. 991–994.

10. Selyanin I. F., Deev V. B., Kukharenko A. V. Resource-saving and environment-saving production technologies of secondary aluminum alloys. Russian Journal of Non-Ferrous Metals. 2015. Vol. 56. Iss. 3. pp. 272–276.
11. Sizyakov V. M., Bazhin V. Yu.,Vlasov A. A. Status and prospects for growth of the aluminum industry. Metallurgist. 2010. Vol. 54. Iss. 7–8. pp. 409–414.
12. Mishra R. K., Venkatesh R. Theoretical evaluation of structural and various associated properties of Al – Si melts. Chemical Physics. 2008. Vol. 354, No. 1–3. pp. 112–117.
13. Pitkowski J. The effect of Al – 17 wt. % Si alloy melt overheating on solidification process and microstructure evolution. Solid State Phenomena. 2011. Vol. 176. pp. 29–34.
14. Shittu M. D., Ibitoye S. A., Olawale J. O., Popoola A. P. I. Superheat influence on mechanical properties of cast hy-poeutectic aluminium-silicon alloy. Int. J. Cast Met. Res. 2012. Vol. 25, No. 3. pp. 170–175.
15. Pitkowski J., Gajdzik B., Matua T. Crystallization and structure of cast A390.0 alloy with melt overheating temperature. Metalurgija. 2012. Vol. 51, No. 3. pp. 321–324.
16. Kolonakov A. A., Kucharenko A. V., Deev V. B., Abaturova A. A. Structure and chemical composition of the AK12MMgN piston alloy fabricated based on various charges. Russian Journal of Non-Ferrous Metals. 2015. Vol. 56. Iss. 4. pp. 428–433.
17. Chaykina N. V., Chaykin V. A., Zadrutskiy S. P., Nemenenok B. M., Rozum V. A. Carbonates — promising materials for the manufacture of refining additives for silumin. Lite i metallurgiya. 2010. No. 3 (57). pp. 33–39.
18. Leushin I. O., Korovin V. A., Novoselov V. V., Pryanichnikov V. A., Smirnova L. A., Moshnin D. A. Modifying mixture. Patent RF, No. 2298047. Applied: 06.06.2005. Published: 27.04.2007. Bulletin No. 12.
19. Bobryshev B. L., Moiseev V. S., Ryakhovskiy A. P., Petrov I. A., Shlyaptse
va A. D., Valiakhmetov S. A., Andreeva M. Yu., Popkov D. V. A method for modifying aluminum-silicon alloys. Patent RF, No. 2623966. Applied: 23.12.2015. Published: 27.06.2017. Bulletin No. 18.
20. Nikitin Yu. P., Lanina Z. N., Akhmetov T. G., Nadeeva F. I., Timoshkin V. I., Sidorchuk V. A., Stepanyan A. G., Mustafin Kh. V., Polyakov E. V., Polyakov M. V. Flux for processing aluminum-silicon alloys. Patent USSR, No. 1673620. Applied: 18.09.1989. Published: 30.08.1991. Bulletin No. 32.
21. Zykovich I. L., Chaykina N. V., Zadrutskiy S. P., Rozum V. A., Panasyugin A. S., Bezhok A. P. Refining treatment of aluminum with calcium carbonate. Polzunovskiy almanakh. 2011. No. 4. pp. 126–128.
22. Beloglazov I. I., Bazhin V. Yu., Zyryanova O. V. Upgrading of the process of technological pulp separation in modern pressure filters. Non-ferrous Metals. 2016. No. 1, pp. 38–40.
23. Kurdyumov A. V., Inkin S. V., Chulkov V. S., Grafas N. I. Flux treatment and filtration of aluminum melts. Moscow : Metallurgiya, 1980. 196 p.
24. Koemets N. A., Nazarova T. N., Rutman D. S., Kashcheev I. D. Composition for impregnating woven glass fibers. Patent USSR, No. 1227609. Applied: 24.10.1983. Published: 30.04.1986. Bulletin No. 16.
25. Available at: bellit.ru/кремнеземные-фильтры/фильтр-фэа.php (accessed: 03.02.2018).
26. Maslov K. A., Leushin I. O., Grachev A. N., Leushina L. I. Flux for refining aluminum alloys. Patent RF, No 2561948 Russia. Applied: 01.04.2014. Published: 10.09.2015. Bulletin No. 25.
27. Grachev A. N., Leushin I. O., Maslov K. A., Leushina L. I. Application of salt hardening bath sludge for aluminum alloy refining. Tsvetnye Metally. 2015. No. 11. pp. 76–79.
28. Nikitin K. V. Modification and complex processing of silumin: study manual. 2nd ed. Samara: Samarskiy gossudarstvennyi tekhnicheskiy universitet, 2016. 92 p.

Language of full-text russian
Full content Buy
Back